1060 aluminum plate and 1070 aluminum plate are pure aluminum alloy, one aluminum content is 97%, one is 96% mostly pure aluminum series, 1 series, the main one is that the 1070 alloy aluminum plate is better than the 1060 aluminum plate when doing the 0 state. The reason is because the higher the aluminum content, the softer the material.
1060 aluminum sheet processing strengthening is also called cold work hardening, which is cold deformation processing of metal materials below recrystallization temperature, such as forging, calendering, drawing, stretching, etc. When cold deformation, the internal dislocation density of the metal increases, and they are intertwined and Form a cellular structure that hinders dislocation motion. The greater the degree of deformation, the more serious the dislocation entanglement, the greater the deformation resistance and the higher the strength. The degree of strengthening after cold deformation varies with the degree of deformation, the deformation temperature of the 1060 pure aluminum plate, and the nature of the material itself. When the same material is cold-deformed at the same temperature, the greater the degree of deformation, the higher the strength and the lower the plasticity. Solid solution strengthened aluminum plate
The addition of certain alloying elements to the pure aluminum 1060 hot-rolled aluminum sheet to form an infinite solid solution or a finite solid solution not only achieves high strength, but also achieves excellent plasticity and good press workability. The alloying elements commonly used for solid solution strengthening in general aluminum alloys are elements such as copper, magnesium, manganese, zinc, silicon, and nickel. Generally, the alloying of aluminum forms a limited solid solution, and binary alloys such as Al-Cu, Al-Mg, Al-Zn, Al-Si, and Al-Mn form a limited solid solution, and both have a large limit solubility. Large solid solution strengthening effect 1060 pure aluminum plate.
1070 aluminum plate has the characteristics of high plasticity, corrosion resistance, good electrical conductivity and thermal conductivity, but its strength is low, it is not strengthened by heat treatment, and its machinability is not good. It can accept contact welding and gas welding. Many advantages are used to manufacture some structural parts with specific properties, such as gaskets and capacitors made of aluminum foil, electronic tube isolation nets, wire and cable protective covers, nets, cores and aircraft ventilation system parts and decorative parts.
Henan Chalco Aluminum Industry Co., Ltd. is a large aluminum plate manufacturer that produces 1060 hot rolled aluminum sheets and 1070 hot rolled aluminum sheets. The width can reach 2600mm. The price is affordable. Welcome to consult.
1060 aluminum sheet processing strengthening is also called cold work hardening, which is cold deformation processing of metal materials below recrystallization temperature, such as forging, calendering, drawing, stretching, etc. When cold deformation, the internal dislocation density of the metal increases, and they are intertwined and Form a cellular structure that hinders dislocation motion. The greater the degree of deformation, the more serious the dislocation entanglement, the greater the deformation resistance and the higher the strength. The degree of strengthening after cold deformation varies with the degree of deformation, the deformation temperature of the 1060 pure aluminum plate, and the nature of the material itself. When the same material is cold-deformed at the same temperature, the greater the degree of deformation, the higher the strength and the lower the plasticity. Solid solution strengthened aluminum plate
The addition of certain alloying elements to the pure aluminum 1060 hot-rolled aluminum sheet to form an infinite solid solution or a finite solid solution not only achieves high strength, but also achieves excellent plasticity and good press workability. The alloying elements commonly used for solid solution strengthening in general aluminum alloys are elements such as copper, magnesium, manganese, zinc, silicon, and nickel. Generally, the alloying of aluminum forms a limited solid solution, and binary alloys such as Al-Cu, Al-Mg, Al-Zn, Al-Si, and Al-Mn form a limited solid solution, and both have a large limit solubility. Large solid solution strengthening effect 1060 pure aluminum plate.
1070 aluminum plate has the characteristics of high plasticity, corrosion resistance, good electrical conductivity and thermal conductivity, but its strength is low, it is not strengthened by heat treatment, and its machinability is not good. It can accept contact welding and gas welding. Many advantages are used to manufacture some structural parts with specific properties, such as gaskets and capacitors made of aluminum foil, electronic tube isolation nets, wire and cable protective covers, nets, cores and aircraft ventilation system parts and decorative parts.
Henan Chalco Aluminum Industry Co., Ltd. is a large aluminum plate manufacturer that produces 1060 hot rolled aluminum sheets and 1070 hot rolled aluminum sheets. The width can reach 2600mm. The price is affordable. Welcome to consult.